HXF-6 化学品防护服

耐磨损性能

Abrasion resistance

测试方法GB24539-2021附录J

Test Method:GB24539-2021AppendisJ

6/6

耐屈绕破坏性能

Fexing resistance

测试方法： GB24539-2021附录K

Test Method:GB24539-2021Appendix K

6/6

抗刺穿性能

Puncture resistance

测试方法；GB/T20655

Test Method:GB/T20655

3/6

耐低温性能

Low temperature resistance

测试方法： GB24539-2021第6.27条

面料经过-40℃预处理8h后，断裂强力下降应不大于30%。     Test Method Aricle 6.27 of GB24539-2021

After the fabric ispretreated at-40°Cfor 8 hours,the breaking strengh shoukd be roducod by no more than 30%.

纵向强力下降： -9.1%

横向强力下降：3.0%

Longirudinal Strength Drop:-9.1%

Lateral Strength Drop:3.0%

耐高温性能

High temperature resistance

测试方法： GB24539-2021第6.27条

面料经过70℃预处理8后，断裂强力下降应不大于30%,

Test Method:Article 6.27 ofGB24539-2021

After the fabric is pretreated at70°C for8hours,the breaking strength should be reduced by no more than 30%.

纵向强力下降： -18.2%

横向强力下降；0.0%

Longitudinal Strength Drop:-18.2%

Lateral Srengh Drop:0.0%

撕破强力Tear strength

测试方法Test Method:GB/T3917.3

4/6

断裂强力Tensile stength

测试方法Test Mchod;GB/T3923.1条样法Suip samples

6/6

按缝强力Seam strengh

测试方法Test Method;GB/T13773.2

5/6

液体耐压穿透性能

Liquid pressure resistance and penetration

面料

Fabric

测试方法；

GB24539-2021附录F

Test Method:

GB24539-2021 Appendix F

30%氢氧化钠30%sodium hydroside

6/6

96%硫酸96%sulfuric acid

65%硝酸65%nitric acid

接缝

seam

30%氢氧化钠30%sodium hydroxide

96%硫酸96%sufuric acid

65%硝酸65%nitric acid

渗透性能

Permeation time

面料Fabric

测试方法；GB/T 23462

Test Method:GB/T23462

96%硫酸在标准渗透量

=2.5 ug/cm2下的标准透过时间

Standard permeability time of96%sufuric acid at standard permeation=2.5ug/cm2

4/6

接 缝 S e a m

拒液性能

(适用4型化学防护服)

Liquid resistance

(applicable for type4)

≥1级(拒液指数>80%

穿透指数<10%)

>Class 1(Liquid rejection index>80%,penetration

index<10%)

测试方法：

GB24539-2021附录I

Test Method:

GB24539-2021 AppendixI

30%硫酸30%sulfuric acid

3/6